Effect of vanadium on grain boundary segregation of phosphorus in low alloy steels

The phosphorus grain boundary segregation at 853 K was investigated in three low alloy steels with different vanadium content. Kinetic dependence of the phosphorus grain boundary concentration was determined experimentally by means of AES and described theoretically, as well. To assess the influence of the individual alloying elements on the phosphorus segregation, the metal composition of carbide phases at 853 K was predicted by means of thermodynamic calculations and confirmed by experimental measurements (TEM + EDX). The vanadium was found to enhance the phosphorus grain boundary segregation by reducing the amount of dissolved and segregated carbon. Thereby, the equilibrium of mutual displacement C (segregated) ? P (segregated) was shifted to more phosphorus segregation. The results achieved indicate that vanadium indirectly increases sensitivity of low alloy steels to intergranular embrittlement.