Effect of octene content on peroxide crosslinking of ethylene–octene copolymers

Various ethylene–octene copolymers were crosslinked by dicumyl peroxide. Octene content was 16, 20, 30, 35 and 38 wt% and melt flow index was 1 or 3 g/10 min. The concentration of dicumyl peroxide was 0.3, 0.5 and 0.7 wt%. Crosslinking was analyzed by a rubber process analyzer in the temperature range 150–200 °C. Cross‐linkability was evaluated from the real part modulus s'_max versus peroxide level plots as the slope of the line. With decreasing octene content and increasing melt flow index the crosslinkability increased. This was confirmed also by tan δ analysis. The network density was measured by the gel content. A higher gel content was found for melt flow index 3 and low octene content. The melting points T_m and the crystallinities were evaluated by DSC. © 2012 Society of Chemical Industry