Subsolidus Relations in the La2O3─CuO─CaO Phase Diagram and the La2O3─CuO Binary Join

The phase diagram for the CuO-rich part of the La₂O₃─CuO join was redetermined. La₂Cu₂O₅ was found to have a lower limit of stability at 1002°± 5°C and an incongruent melting temperature of ～1035°C. LagCu₇O₁₉ had both a lower (1012°± 5°C) and an upper (1027°± 5°C) limit of stability. Subsolidus phase relations were studied in the La₂O₃─CuO─CaO system at 1000°, 1020°, and 1050°C in air. Two ternary phases, La_1.9Ca_1.1Cu₂O_5.9 and LaCa₂Cu₃O_8.6, were stable at these temperatures, with three binary phases, Ca₂CuO₃, CaCu₂O₃, and La₂CuO₄. La₂Cu₂O₅ and La₈Cu₇O₁₉ were stable only at 1020°C, and did not support solid-solution formation.