Formation of Phosphorous Surface Inverse Segregation in Twin-Roll Cast Strips of Low-Carbon Steels |
| |
Authors: | ZHOU Guo-ping LIU Zhen-yu YU Shi-chuan CHEN Jun QIU Yi-qing WANG Guo-dong |
| |
Affiliation: | 1. Strip Cold Rolling Plant, Tangshan Iron and Steel Group, Tangshan 063016, Hebei, China 2. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China |
| |
Abstract: | The formation of phosphorous surface inverse segregation (SlS) in twin-roll cast strips of low-carbon steels was studied. High phosphorous strips were fabricated by using a pilot twin-roll strip caster and a melt/substrate contacting apparatus, respectively. Solidification structures of strips were observed and analyzed, and phosphorus distributions along longitudinal sections of strips were investigated and discussed. The results showed that solidification structures of all strips were columnar grains, either integrated or coarse in the strip made by the melt/substrate contacting apparatus or damaged in some degree in cast strips; and that during cast strip solidification, enrichment of phosphorus occurred between columnar grains, and the average phosphorus concentration near the surface in the strip with 0. 15% of phosphorus was measured to be about 0. 27% which was oiviously higher than that in the bulk. |
| |
Keywords: | strip casting phosphorus enrichment inverse segregation steel solidification |
本文献已被 维普 万方数据 等数据库收录! |
| 点击此处可从《钢铁研究学报(英文版)》浏览原始摘要信息 |
|
点击此处可从《钢铁研究学报(英文版)》下载全文 |
|