| 高碳82B线材控轧控冷工艺优化实践 |
| |
| 引用本文： | 李长胜,马志军,王 进,等.高碳82B线材控轧控冷工艺优化实践[J].山东冶金,2014(1):20-21. |
| |
| 作者姓名： | 李长胜 马志军 王 进 等 |
| |
| 作者单位： | 张家港联峰钢铁研究所有限公司,江苏张家港215628 |
| |
| 摘 要： | 对82B线材控轧控冷工艺进行了优化,通过改变终轧温度、吐丝温度和斯太尔摩辊道速度及冷却工艺参数,盘条的组织和力学性能基本达到了使用要求,索氏体化率达到85%以上,月产量稳定在5 000 t以上。
|
| 关 键 词： | 82B线材 控轧控冷 索氏体 |
Optimization Practice on Controlled Rolling and Controlled Cooling Process of High Carbon 82B Wire Rod |
| |
| LI Changsheng,MA Zhijun,WANG Jin,ZHANG Xianyi.Optimization Practice on Controlled Rolling and Controlled Cooling Process of High Carbon 82B Wire Rod[J].Shandong Metallurgy,2014(1):20-21. |
| |
| Authors: | LI Changsheng MA Zhijun WANG Jin ZHANG Xianyi |
| |
| Affiliation: | (Zhangjiagang Lianfeng Iron and Steel Research Institute Co., Ltd., Zhangjiagang 215628, China) |
| |
| Abstract: | Controlled rolling and controlled cooling process is explored for 82B wire rod. Through changing the finishing temperature, laying temperature and stelmor roller speed process parameter, the microstructure and mechanical property of wire rod has basically reached the expected result, sorbitizing rate reached 85%above and the monthly output stabilized at above 5 000 t. |
| |
| Keywords: | 82B wire rod controlled rolling and controlled cooling process sorbite |