| Abstract: | This study was conducted to determine the effect of clay content in GFRP (glass‐fiber‐reinforced polymer) composite samples as they were aged in an alkaline solution. Two kinds of GFRP composite samples were prepared. One was E‐glass‐fiber‐reinforced vinyl ester polymer, and the other was nano‐GFRP composites prepared with the addition of 1 and 2 wt% of montmorillonite clay to the polymer matrix. These samples were aged in alkaline solution of pH 13.2 with and without sustained load. The load was 1335 N or 18.7% of the tensile strength of the composite samples. The aging was evaluated by measuring the reduction in tensile strength after 6 months. Also, absorption of alkaline solution into the plain and nano‐GFRP samples was investigated so as to elucidate the diffusion behaviors. It was found that for a short exposure time (e.g. 1 month) and without sustained load, dispersing 2 wt% of the nanoclay in the polymer matrix of the GFRP samples reduces the diffusivity by 39%. However, with the application of sustained load, the glass fiber composite samples deteriorate more with increasing clay content. The reduction in tensile strength was 7.1%, 12.1%, and 18.1% for the samples containing 0, 1, and 2 wt% of clay, respectively. J. VINYL. ADDIT. TECHNOL., 12:25–32, 2006. © 2006 Society of Plastics Engineers |