Fabrication of TiO2 nanotubes by anodization of Ti thin films for VOC sensing

Ti thin films were anodized in aqueous HF (0.5 wt.%) and in polar organic (0.5 wt.% NH₄F + ethylene glycol) electrolytes to form TiO₂ nanotube arrays. Ti thin films were deposited on microscope glass substrates and then anodized. Anodization was performed at potentials ranging from 5 V to 20 V for the aqueous HF and from 20 V to 60 V for the polar organic electrolytes over the temperatures range from 0 to 20 °C. The TiO₂ nanotubes were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) and energy dispersive X-ray spectroscopy (EDX). It has been observed that anodization of the deposited Ti thin films with aqueous HF solution at 0 °C resulted in nanotube-type structures with diameters in the range of 30-80 nm for an applied voltage of 10 V. In addition, the nanotube-type structure is observed for polar organic electrolyte at room temperature at the anodization voltage higher than 40 V. The volatile organic compound (VOC) sensing properties of TiO₂ nanotubes fabricated using different electrolytes were investigated at 200 °C. The maximum sensor response is obtained for carbon tetrachloride. The sensor response is dependent on porosity of TiO₂. The highest sensor response is observed for TiO₂ nanotubes which are synthesized using aqueous HF electrolyte and have very high porosity.