Influence of martensite content and morphology on the toughness and fatigue behavior of high-martensite dual-phase steels

A series of high-martensite dual-phase (HMDP) steels exhibiting a 0.3 to 0.8 volume fraction of martensite (V _m ), produced by intermediate quenching (IQ) of a vanadium and boron-containing microalloyed steel, have been studied for toughness and fatigue behavior to supplement the contents of a recent report by the present authors on the unusual tensile behavior of these steels. The studies included assessment of the quasi-static and dynamic fracture toughness and fatigue-crack growth (FCG) behavior of the developed steels. The experimental results show that the quasi-static fracturetoughness (K _ICV ) increases with increasing V _m in the range between V _m =0.3 and 0.6 and then decreases, whereas the dynamic fracture-toughness parameters (K _ID , K _D , and J _ID ) exhibit a significant increase in their magnitudes for steels containing 0.45 to 0.60 V _m before achieving a saturation plateau. Both the quasi-static and dynamic fracture-toughness values exhibit the best range of toughnesses for specimens containing approximately equal amounts of precipitate-free ferrite and martensite in a refined microstructural state. The magnitudes of the fatigue threshold in HMDP steels, for V _m between 0.55 and 0.60, appear to be superior to those of structural steels of a similar strength level. The Paris-law exponents (m) for the developed HMDP steels increase with increasing V _m , with an attendant decrease in the pre-exponential factor (C).