Electrochemical performance of LiCoO2 cathodes by surface modification using lanthanum aluminum garnet

LiCoO₂ particles were coated with various wt.% of lanthanum aluminum garnets (3LaAlO₃:Al₂O₃) by an in situ sol–gel process, followed by calcination at 1123 K for 12 h in air. X-ray diffraction (XRD) patterns confirmed the formation of a 3LaAlO₃:Al₂O₃ compound and the in situ sol–gel process synthesized 3LaAlO₃:Al₂O₃-coated LiCoO₂ was a single-phase hexagonal α-NaFeO₂-type structure of the core material without any modification. Scanning electron microscope (SEM) images revealed a modification of the surface of the cathode particles. Transmission electron microscope (TEM) images exposed that the surface of the core material was coated with a uniform compact layer of 3LaAlO₃:Al₂O₃, which had an average thickness of 40 nm. Galvanostatic cycling studies demonstrated that the 1.0 wt.% 3LaAlO₃:Al₂O₃-coated LiCoO₂ cathode showed excellent cycle stability of 182 cycles, which was much higher than the 38 cycles sustained by the pristine LiCoO₂ cathode material when it was charged at 4.4 V.