Structural changes of bare and AlPO4-coated LixCoO2 (x = 0.24 and 0.1) upon thermal annealing ≥200°C

Structural changes of bare and AlPO₄-coated Li_xCoO₂ with a coating thickness of 20 and 200 nm are investigated at x = 0.24 and 0.1 after thermal annealing at 200, 300, and 400 °C using XRD and Co K-edge XANES (X-ray absorption near-edge structure) and EXAFS (extended X-ray absorption fine structure). Both the bare and coated cathodes exhibit faster phase transformation into spinel phases at lower annealing temperatures as x in Li_xCoO₂ is decreased. Bare Li_xCoO₂ cathodes exhibit phase transitions from Li_xCo₂O₄ to Co₃O₄ spinel as the annealing temperature is increased and the x is value decreased, which suggests a possible reaction according to (1/2)Li_xCo₂O₄ → xLi₂CO₃ + (1/3)Co₃O₄ + (2/3)O₂. However, the coated cathodes sustain a Li_xCo₂O₄ phase even at 400 °C and x = 0.1. This indicates that the AlPO₄ coating layer suppresses the Li_xCo₂O₄ phase decomposition into Co₃O₄.