Thermal diffusivity measurements of some synthetic CaO-Al2O3-SiO2 slags

In an attempt to systematize the knowledge of the heat conduction of liquid silicates, the effective thermal diffusivities of some synthetic slags containing CaO, Al₂O₃, and SiO₂ have been measured, using the three-layer laser-flash method on a differential scheme in the temperature range of 1625 to 1825 K. The effective thermal diffusivities measured, which are a combination of the phononic and photonic heat-transfer mechanisms, were found to increase with increasing temperature for all the presently investigated slags. The slag compositions were chosen in such a way that the changes in the effective thermal diffusivities would reflect the changes in the structure of the slags. It was observed that, at a CaO/Al₂O₃ molar ratio of 4.42, an increase of the SiO₂ content had very little effect on the effective thermal diffusivity values. On the other hand, addition of SiO₂ to a slag with the CaO/Al₂O₃ molar ratio of 2.59 resulted in a significant increase in the effective thermal diffusivity. The addition of Al₂O₃ to slags with a constant CaO/SiO₂ molar ratio resulted in a marked increase in the effective thermal diffusivity. Both these trends indicate that there might be an influence of the network formation in silicate melts on the effective thermal diffusivity.