(Bi1/2Na1/2)TiO3–Ba(Cu1/2W1/2)O3 Lead-Free Piezoelectric Ceramics

(Bi_1/2Na_1/2)TiO₃ with 0–6 mol% Ba(Cu_1/2W_1/2)O₃ (BNT-BCW), a new member of the BNT-based group, has been prepared following the conventional mixed oxide route. The compacted bodies were sintered at 1130°C for 2 h to get dense ceramics. The addition of BCW into BNT ceramics facilitated the poling process because of a reduction in leakage current. 0.995BNT·0.005BCW ceramics exhibit a relatively high piezoelectric constant ( d ₃₃= 80 × 10^?12 C/N) and a relatively low dielectric loss (tan δ= 1.5%). Increased amount of BCW was found to increase the dielectric constant and loss of BNT-BCW ceramics and to suppress the grain growth. During sintering, some BCW diffuses into the lattice of BNT to form a solid solution and some remains on the grain boundaries.