Siloxane‐modified polyacrylate low‐residual pressure‐sensitive adhesive with high peeling strength |
| |
| Authors: | Pengjuan Li Fuwei Nian Min Zhang Minmin Shen Yongqiang Dai Hao Pang Bing Liao |
| |
| Affiliation: | 1. Key Laboratory of Cellulose and Lignocelluloses Chemistry, Guangzhou Institute of Chemistry, Chinese Academy of Sciences, 368 Xingke Rd, Tianhe District, Guangzhou, China;2. University of Chinese Academy of Sciences, 19 Yuquan Rd, Shijingshan District, Beijing, China;3. Foshan University, 15 Jiangwan Rd, Chancheng District, Foshan, 528000, Foshan, China;4. Guangzhou Guangzhou Institute of Chemistry Green Building Materials Academy, 368 Xingke Rd, Tianhe District, Guangzhou, China |
| |
| Abstract: | A low‐residual siloxane‐modified polyacrylate pressure‐sensitive adhesive (PSA) with a high peeling strength was prepared by seeded semicontinuous emulsion polymerization. 3‐Glycidyloxypropyltrimethoxysilane was introduced into the acrylic (AC) PSA through a thermal posttreatment method to crosslink with AC. To improve the adhesion properties, a polymeric emulsifier, 2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid, was introduced into the system with the conventional emulsifier. Several key polymerization conditions, such as the initiator concentration, mass ratio of soft monomer to hard monomer, the content of polymeric emulsifier, and siloxane dosages were examined in detail. Then, the optimal conditions and a proper preparation process were established. The results show that we achieved not only a low repeeling residue with high tack and peeling strength but also excellent properties of high‐temperature aging resistance and water resistance. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 42975. |
| |
| Keywords: | high peeling strength low residue organic siloxane polyacrylate pressure‐sensitive adhesive (PSA) |
|
|