Edge defect analysis of high-strength corrosion-resistant steel |
| |
Affiliation: | Research Institute, Baoshan Iron & Steel Co., Ltd., Shanghai 201900, China |
| |
Abstract: | In this study,a 600 MPa hot-rolled corrosion-resistant steel plate produced by a specific company is investigated. Edge jagged defects and edge surface defects generated on both sides of the strip during production are characterized and analyzed. The results indicate that the distribution of reoxidation granules is located underneath the surface peel and that copper-containing granules diffuse along austenite grain boundaries. This phenomenon combined with the chemical composition and production parameters of a strip indicate that copper brittleness leads to edge jagged defects. However,the surface defects should be attributed to inherent defects on the surface of the strip. Measures that prevent surface oxidation and copper segregation at grain boundaries would likely eliminate these two types of edge defects. |
| |
Keywords: | edge defect high-strength steel corrosion-resistant steel copper brittleness |
本文献已被 CNKI 万方数据 等数据库收录! |
|