| 低碳包晶钢连铸工艺设计及纵裂纹控制 |
| |
| 引用本文： | 马勤学.低碳包晶钢连铸工艺设计及纵裂纹控制[J].炼钢,2000,16(5):28-30,50. |
| |
| 作者姓名： | 马勤学 |
| |
| 作者单位： | 武汉钢铁集团公司 |
| |
| 摘 要： | 重点论述了低碳包晶钢连铸时的特殊性引发的连铸坯裂纹问题，分析了此类纵裂纹缺陷的特点及产生原因，根据武钢三炼钢厂在低碳包晶钢纵裂控制方面的生产实践，提出了浇铸低碳包晶铸钢时的连铸工艺控制技术，取得了显著成效。
|
| 关 键 词： | 低碳包晶钢 连铸 工艺设计 纵裂纹控制 |
Design of Continuous Casting Technology for Low Carbon Peritectic Steel and Control of Longitudinal Cracks |
| |
| Ma Qinxue.Design of Continuous Casting Technology for Low Carbon Peritectic Steel and Control of Longitudinal Cracks[J].Steelmaking,2000,16(5):28-30,50. |
| |
| Authors: | Ma Qinxue |
| |
| Abstract: | This paper emphatically discusses the longitudinal Cracks in Continuously cast slabs caused by specificity of continuously casting low carbon peritectic steel, and analyzes the cause and characteristics of the occurrence of these kinds of longitudinal cracks. Combining with the experiences of the control on longitudinal cracks in low carbon peritectic steel in No.3 Steelmaking Plant of WISCO, a new plan for continuous casting process and control techique during casting low carbon peritectic steel has been put forward, which has achieved significantly good results. |
| |
| Keywords: | low carbon peritectic steel characteristics of ongitudinal crack design of continuous casting technique control of longitudinal crack |