Mechanochemical block copolymerization in heterogeneous systems of the solid poly(vinyl chloride) with styrene by ultrasonic irradiation

Summary Mechanochemical block copolymerization in heterogeneous systems of the solid poly(vinyl chloride)-styrene-sodium dodecyl sulfate aqueous solutions has been studied by ultrasonic irradiation at 65 °C. The block copolymerization of styrene was initiated by free radicals produced from the poly(vinyl chloride) particles by ultrasonic waves. The initial rate of the block copolymerization Rp was given by Rp α [Styrene] [Sodium dodecyl sulfate]^1/2. Both copolymer and homopolymer were obtained. For example, when 2.506 g of the poly(vinyl chloride) particles, 24.23 g of styrene, and 54.00 g of sodium dodecyl sulfate aqueous solution (0.500 wt%) were added in the reaction system, the weight proportions of the block copolymer and polystyrene after 60 min were approximately 50 and 20%.