P92钢焊接接头的组织和性能研究 |
| |
引用本文: | 李俊,张忠文. P92钢焊接接头的组织和性能研究[J]. 山东电力技术, 2009, 0(3): 28-30 |
| |
作者姓名: | 李俊 张忠文 |
| |
作者单位: | 中国石化集团第十建设公司,山东,淄博,255438;山东电力研究院,山东,济南,250002 |
| |
摘 要: | 通过硬度试验、冲击试验、断口扫描和金相组织观察,研究了P92钢焊接接头的性能、组织特点及关系。结果表明,焊缝的硬度比HAZ的大,冲击功比HAZ的小;二者在断裂形态上的差异导致了两个部位对冲击吸收功的不同;焊缝金属组织中形成的奥氏体枝晶是造成焊缝金属的韧性明显低于HAZ的主要因素之一。
|
关 键 词: | P92钢 焊接接头 焊缝 HAZ 冲击韧性 |
Study on Microstructure and Property of P92 Welding Joint |
| |
Abstract: | Based on hardness test, impact test, SEM of impacted fracture surface and microstructure observation, microstructure and property of P92 welding joint as well as their relationship were studied. The result shows that weld metal presents higher hardness and lower impact toughness than HAZ. The difference of fracture appearance between weld metal and HAZ leads to different impacting energy. The dendritic austenite grain in weld metal is one of key factors to cause the impact toughness of weld metal much lower... |
| |
Keywords: | P92 steel welding joint weld metal HAZ impact toughness |