Evaluation of surface residual stresses in HVOF sprayed WC-12Co coatings by XRD and ED-hole drilling

Thermally sprayed coatings are inherently associated with residual stresses in the coatings. These stresses have a noticeable effect on the physical and mechanical properties of coatings. The high speed hole drilling method is widely used to measure the residual stress. Due to the nature of the thermally sprayed coatings, the application of this method for WC/Co coatings has some limitations. In the current study, WC-12Co coatings were deposited using HVOF thermal spraying. The electro discharge hole drilling method was developed to measure the through thickness residual stress in WC-Co thermally sprayed coatings. Morphological studies were conducted using optical microscopy and scanning electron microscopy (SEM) to evaluate the powder and coating characteristics. The sin²ψ method was used to evaluate the surface residual stress by means of XRD. The residual stress at the surface using EDM and XRD was approximately ?32.54 MPa and ?40.6 MPa respectively. The experimental results reveal that the stress curves are not uniform through the coating thickness. It has been found that the mean residual stress is of approximately ?126 MPa. Obtained results are in good agreement with the reported values from literatures. The developed method confirms the feasibility of residual stresses measurement for HVOF thermally sprayed WC-Co coatings.