2.5维机织复合材料疲劳寿命预测 |
| |
引用本文: | 单宏伟,周光明.2.5维机织复合材料疲劳寿命预测[J].玻璃纤维,2015(5). |
| |
作者姓名: | 单宏伟 周光明 |
| |
作者单位: | 南京航空航天大学,南京,210016 |
| |
摘 要: | 对2.5维机织复合材料进行了静力分析,在受拉伸载荷的情况下将其视为经纱层和纬纱层组合而成的层合板。以单向板疲劳寿命预测为基础,考虑到疲劳加载过程中刚度退化导致的应力重新分配,采用Miner理论对其拉-拉疲劳寿命进行预测,且对该方法进行了试验验证,为预测2.5维机织复合材料的疲劳寿命提供了一种途径。
|
关 键 词: | 2.5维机织复合材料 静力分析 疲劳寿命 刚度退化 Miner理论 |
Fatigue Life Prediction for 2 . 5 D Woven Composites |
| |
Abstract: | 2. 5-dimensional woven composite was subjected to static loading, and it was regarded as a laminate consisting of warp layer and weft layer under tensile loading. Based on the fatigue life prediction of unidirectional laminate , the fatigue life of 2 . 5-dimensional composites was predicted by using Miner Theory of linear fatigue dam-age accumulation and considering the stress redistribution resulting from the degradation of stiffness in the process of fatigue loading. The verification experiment result of tensile-tensile fatigue loading conformed to the prediction re-sult. This paper provides a new method for predicting the fatigue life of 2. 5-dimensional woven composites. |
| |
Keywords: | 2 5-dimensional woven composite static loading analysis fatigue life degradation of stiffness Miner Theory |
本文献已被 CNKI 万方数据 等数据库收录! |
|