High cycle fatigue behavior of DP980 steel and DP980 steel laser welded joints

For the study of the DP980 steel high cycle fatigue property, high fatigue tests of DP980 steel and DP980 steel laser welded joints were carried out with fatigue testing machine, the Basquin equation was concluded. Microstructures and fractures were analyzed by optical microscope and scanning electron microscope. The results show that DP980 steel laser welding joints have the weld concavity at the welding root and top, the quality of welded joints is medium. The fatigue limit of DP980 steel is 341MPa, the fatigue limit of DP980 steel laser welded joint is 148MPa, the fatigue limit decreases by 50% compared with the fatigue limit of the base metal. For DP980 steel, the crystal boundary of the ferrite/martensite is the main location of micro cracks initiation, the fatigue fracture of DP980 steel is the quasi cleavage fracture. For DP980 steel laser welding joints, the fatigue cracks initiation is located in the weld concavity, not in the heat affected zone, the fatigue fracture is cleavage fracture. DP980 steel and DP980 steel laser welding joints crack propagation is characterized by the obviously fatigue striations coupled with secondary cracks.