A study on carbon coating to silicon and electrochemical characteristics of Si-C/Li cells

The aim of this paper is to study the electrochemical behavior of Si-C material synthesized by heating a mixture of silicon and polyvinylidene fluoride (PVDF) in the ratios of 5, 20, and 50 wt%. The particle size of the synthesized material was found to be increased with increase in the PVDF ratio. The coexistence of silicon with carbon was confirmed from the XRD analysis. A field emission scanning electron microscope (FESEM) study performed with the material proved the improvement in coating efficiency with increase in the PVDF ratio. Coin cells of the type 2025 were made by using the synthesized material, and the electrochemical properties were studied. An electrode was prepared by using the developed Si-C material. Si-C|Li cells were made with this electrode. A charge|discharge test was performed for 20 cycles at 0.1 C hour rate. Initial charge and discharge capacities of Si-C material derived from 20 wt% of PVDF was found to be 1,830 and 526 mAh|g, respectively. Initial charge/discharge characteristics of the electrode were analyzed. The level of reversible specific capacity was about 216mAh/g at Si-C material derived from 20 wt% of PVDF, initial intercalation efficiency (IIE), intercalation efficiency at initial charge/discharge, was 68%. Surface irreversible specific capacity was 31 mAh/g, and average specific resistance was 2.6 ohm * g.