Preparation and performances of mesoporous TiO2 film photocatalyst supported on stainless steel

Mesoporous TiO₂ film photocatalysts supported on stainless steel substrates were prepared using the sol–gel method with Ti(OC₄H₉)₄ as a precursor and poly ethylene glycol (PEG) as a structure-directing agent. Mesoporous TiO₂ film with a pore diameter of about 15 nm was obtained with the addition of PEG (molecular WEIGHT =400). The pore diameter of TiO₂film was varied with molecular weight of PEG additive. The structure-directing process was also discussed. Mesoscopically ordered inorganic/polymer composites were believed to form during the process. Compared to conventional TiO₂ film photocatalyst, the mesoporous TiO₂ film showed a good performance for the photo degradation of rhodamine B (RB) solution irradiated with UV light of 365 nm. The photo degradation constant of rhodamine B for mesoporous TiO₂ film photocatalyst can arrive at 22 times of that for conventional TiO₂ film photocatalyst. Also an excellent performance for the degradation of gaseous formaldehyde with mesoporous film photocatalyst was obtained. The photo degradation rate of gaseous formaldehyde for mesoporous TiO₂ film photocatalyst can arrive at six times of that for conventional TiO₂ film photocatalyst.