Influence of La2O3 addition on microstructure and wear resistance of Fe-Cr-C cladding formed by arc surface welding |
| |
| Authors: | ZHOU Yefei YANG Yulin QI Xiaowen JIANG Yongwen YANG Jian REN Xuejun YANG Qingxiang |
| |
| Affiliation: | 1 (1. State Key Laboratory of Metastable Materials Science & Technology, Yanshan University, Qinhuangdao 066004, China; 2. School of Engineering, Liverpool John Moores University, Liverpool L3 3AF, UK) |
| |
| Abstract: | The Fe-Cr-C claddings formed by arc surface welding with different La2O3 additions were investigated. The microstructures were observed by optical microscopy (OM), field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). The phase structures were measured by X-ray diffraction (XRD). The wear resistances of the claddings were tested by friction and wear experiment. On this basis, the carbide refinement mechanism by inclusion enriched with La was discussed theoretically. The results showed that, the microstructure of the Fe-Cr-C cladding consisted of primary (Cr,Fe)7C3 carbides and eutectic (γ-Fe+(Cr,Fe)7C3 ) structure. With La2O3 addition increasing, the primary carbides were refined, and the mass loss of the cladding decreased gradually. The Fe-Cr-C cladding with 4wt.% La2O3 addition had a best wear resistance behaviour. The RE inclusion LaAlO3 as heterogeneous nuclei of the primary M7C3 was medium effective, and could refine the M7C3 carbides. Besides, the wear resistance could be improved by adding La2O3 in the claddings. |
| |
| Keywords: | Fe-Cr-C cladding rare earth oxide carbides microstructure |
| 本文献已被 CNKI 维普 ScienceDirect 等数据库收录！ |
|