Surface Characterization of Chlorinated Synthetic Vulcanized Styrene-Butadiene Rubber Using Contact Angle Measurements,Infra-Red Spectroscopy and XPS

The surface of a sulfur-vulcanized synthetic styrene-butadiene rubber (SBR) was treated with ethyl acetate solutions containing different amounts of trichloroisocyanuric acid (TCI). The chlorinated SBR surfaces were characterized using contact angle measurements (water, ethane diol, n-hexadecane), infra-red (IR) spectroscopy and XPS. Chlorination produced an increase of surface free energy which was mainly due to the enhancement of the acid-base component of the surface free energy, which remained almost unchanged when the amount of TCI was increased. Depending on the amount of chlorination agent, several chemical species were present on the SBR surface: i) For low amounts of TCI (up to 2 wt%), mainly chlorinated hydrocarbon and C – O species were present on the surface; ii) For medium amounts of TCI (between 2 and 5 wt%), an excess of unreacted TCI remained on the surface and a relatively small amount of isocyanuric acid was deposited; iii) For high amounts of TCI (larger than 5 wt%), a weak boundary layer (mainly composed of isocyanuric acid) was formed on the surface and thus the effects due to chlorination were decreased. There was good agreement between the experimental results obtained with contact angle measurements and XPS because both provided information on a surface region close to 100 Å, whereas IR spectroscopy results showed deeper penetration of the chlorinating agent into the SBR surface. The estimated thickness of the chlorinated layer was near 5000 Å as estimated from XPS measurements of SBR surfaces modified by argon ion bombardment.