Treatment of thermoplastic rubberwith chlorine bleach as an alternative halogenation treatment in the footwear industry |
| |
| Authors: | C M Cepeda-Jiménez M M Pastor-Blas J M Martín-Martínez P Gottschalk |
| |
| Affiliation: | 1. Adhesion &2. Adhesives Laboratory, Department of Inorganic Chemistry , University of Alicante , Alicante , Spain;3. H. B. Fuller Company Research Corporation , St. Paul , Minnesota , USA |
| |
| Abstract: | Avoidance of solvents in bonding operations is a current demand in the footwear industry. Halogenation of rubber soles with solutions of trichloroisocyanuric acid (TCI) in different solvents has been successfully used to improve bonding to the leather uppers. In this study, the use of chlorine bleach as an alternative water surface treatment for a rubber has been tested. A thermoplastic block styrene thermoplastic (TR) was treated with bleach to improve its adhesion to a water-based polyurethane dispersion adhesive (PUD). T-peel testing, scanning electron microscopy (SEM), contact angle measurements (ethanediol, 25°C), and infrared spectroscopy (ATR-IR) were used to analyze the modifications produced on the rubber surface. Adhesion values were obtained from T-peel testing of joints produced with similarly treated TR rubber test pieces. Different experimental variables were considered in this study, namely the immersion time (0.5-2 min) in bleach, the active chlorine content (43.9- 55.6 g/l) in the bleach, the addition of a wetting agent (1-octyl-2-pyrrolidone) to the bleach, and the application of the surface treatment using an ultrasonic bath. The treatment with bleach produced the chlorination of the hydrocarbon chains on the TR rubber surface and slightly changed the surface roughness. Chlorination of the TR rubber with bleach (free active chlorine=55.6 g/l) was fast and needed only 30 sec immersion in the reagent mixture to produce high adhesion. Furthermore, the active chlorine content in the bleach was critical to assure an adequate T-peel strength value. The addition of 1-octyl-2-pyrrolidone to the bleach increased the wettability of the rubber surface, although it was necessary to carry out the surface treatment in the ultrasonic bath to obtain adequate adhesion to the PUD adhesive. Thermoplastic styrene-butadiene rubber Water-based polyurethane adhesive Bleach Halogenation Water-based surface treatment Contact angle ATR-IR spectroscopy SEM T-peel strength |
| |
| Keywords: | |
|
|