Comparison of Analytical,Numerical, and Experimental Methods in Deriving Fracture Toughness Properties of Adhesives Using Bonded Double Lap Joint Specimens |
| |
Authors: | A R Setoodeh H Hadavinia F R Biglari |
| |
Affiliation: | 1. Mechanical Engineering Department, Imperial College London, South Kensington Campus, United Kingdom and Mechanical Engineering Department , School of Engineering, Ferdowsi University , Mashhad, Iran;2. School of Engineering , Kingston University , London, United Kingdom;3. Mechanical Engineering Department , Amirkabir University of Technology , Tehran, Iran |
| |
Abstract: | Stress and fracture analysis of bonded double lap joint (DLJ) specimens have been investigated in this paper. Numerical and analytical methods have been used to obtain shear- and peel-stress distributions in the DLJ. The generalized analytical solution for the peel stress was calculated for various forms of the DLJ geometry and, by using crack closure integral (CCI) and by means of the J-integral approach, the analytical strain energy-release rate, G, was calculated. Experimental fracture tests have also been conducted to validate the results. The specimens were made of steel substrates bonded by an adhesive and loaded under tension. Specimens with cracks on both sides and at either end of the DLJ interface were tested to compare the fracture behavior for the two crack positions where tensile and compressive peel stresses exist. Tests confirmed that the substrates essentially behave elastically. Therefore, a linear elastic solution for the bonded region of the DLJ was developed. The fracture energy parameter, G, calculated from the elastic experimental compliance for different crack lengths, was compared with numerical and analytical calculations using the experimental fracture loads. The stresses from analytical analysis were also compared with those from the finite element results. The strain energy-release rate for fracture, G f , for the adhesive has been shown to have no R-curve resistance, was relatively independent of crack length, and compared well with those obtained from numerical and analytical solutions. However, it was found that fracture energy for the crack starter in the position where the peel stress was tensile was about 20% lower than where the crack was positioned at the side, where the peel stress was found to be compressive. |
| |
Keywords: | Fracture toughness Compliance method Double lap joint Adhesive |
|
|