| 低碳冷镦钢冷镦开裂原因分析 |
| |
| 引用本文： | 李伟,许立伟,郭景彪. 低碳冷镦钢冷镦开裂原因分析[J]. 机械工程与自动化, 2001, 0(4): 55-56 |
| |
| 作者姓名： | 李伟 许立伟 郭景彪 |
| |
| 作者单位： | 1. 太钢钢研所,山西,太原,030003
2. 太钢初轧厂,山西,太原,030003 |
| |
| 摘 要： | 用低碳冷镦钢制造标准件的过程中,常常出现表面开裂现象,以ML15、SWRM8K为例,研究了低碳冷镦钢经常出现的冷镦开裂形式、产生的原因及防止措施.
|
| 关 键 词： | 低碳钢 冷锻 开裂 分析 |
| 文章编号： | 1008-8342(2001)04-0055-02 |
| 修稿时间： | 2001-05-30 |
Analysis of cracking reasons in the cold heading process of low carbon cold heading steel |
| |
| LI Wei ,XU Li wei ,GUO Jin biao. Analysis of cracking reasons in the cold heading process of low carbon cold heading steel[J]. Mechanical Engineering & Automation, 2001, 0(4): 55-56 |
| |
| Authors: | LI Wei XU Li wei GUO Jin biao |
| |
| Affiliation: | LI Wei 1,XU Li wei 2,GUO Jin biao 1 |
| |
| Abstract: | Superficial cracks often occur in the cold heading process of standard parts made of the low carbon cold heading steel In this article, the authors study the cold heading cracking forms, occurring reasons and preventing measures for low carbon cold heading steels especially for these two steel grades ML15 and SWRM8K |
| |
| Keywords: | low carbon steel cold heading cracking analysis |