We determined the critical deflagration pressure for titanium samples of various form during failure in oxygen. For like samples, we estimated the exposure rate of juvenile metal surface using the results of photographs of crack propagation during failure.
| | 2. |
We proposed an empirical equation which describes the critical deflagration pressure of titanium samples during failure in oxygen, as a function of the rate of exposure of juvenile metal surface.
| | 3. |
We suggested that this dependence of the critical deflagration pressure on sample configuration can be explained by the difference in the rates of exposure of juvenile metal surface during the failure of the titanium samples in oxygen.
|