| 铝合金2007的激光焊接 |
| |
| 引用本文： | 王海林,黄维玲,周卓尤,曹红兵. 铝合金2007的激光焊接[J]. 激光技术, 2003, 27(2): 103-105 |
| |
| 作者姓名： | 王海林 黄维玲 周卓尤 曹红兵 |
| |
| 作者单位： | 1.华中科技大学激光技术国家重点实验室, 武汉, 430074 |
| |
| 摘 要： | 研究了采用高功率Nd:YAG连续激光器焊接铝合金2007的方法和工艺参数。通过观察焊缝截面,发现存在气孔和热裂纹。工艺实验表明,采用填充焊丝AlSi12激光焊接可有效抑制热裂纹的产生。
|
| 关 键 词： | 激光焊接 铝合金 气孔 热裂纹 |
| 文章编号： | 1001-3806(2003)02-0103-03 |
| 收稿时间： | 2002-05-17 |
| 修稿时间： | 2002-05-17 |
Laser welding of aluminum alloy 2007 |
| |
| Wang Hailin,Huang Wiling,Zhou Zhuoyou,Cao Hongbing. Laser welding of aluminum alloy 2007[J]. Laser Technology, 2003, 27(2): 103-105 |
| |
| Authors: | Wang Hailin Huang Wiling Zhou Zhuoyou Cao Hongbing |
| |
| Abstract: | The processing paraments of laser welding of aluminum alloy 2007 with high power Nd:YAG CW laser are studied.Pores and hot cracks are found in the welding seam. The experiments show that laser welding with filler wire Alsi12 cna minimize hot crack due to the smallest amout of heat input into the ease material. |
| |
| Keywords: | laser welding aluminnm alloy porosity hot crack |