| Abstract: | New acrylic rubbers with a pendant epoxy group were prepared by copolymerization of butyl acrylate (BA) with vinylbenzyl glycidyl ether (VBGE). The modification of an epoxy system (bisphenol-A diglycidyl ether/p,p′-diaminodiphenyl sulfone) with the acrylic rubbers was carried out in order to increase the toughness of the cured epoxy resin. The addition of 20 wt.-% of the copolymer containing 74% of BA and 26% of VBGE units resulted in a 30% increase in the fracture toughness (KIC) of the cured resin at minimal expenses of strength and modulus of the resin. The modified epoxy resin had two-phase morphology in which the rubber particles with average diameter of 2 μm are dispersed in the epoxy matrix. The copolymer without the pendant epoxy group, prepared from BA and vinylbenzyl methoxyethyl ether, was ineffective as a modifier, indicating that the reaction of the pendant epoxide with the epoxy matrix resulted in good interfacial adhesion between the rubber particles and the matrix, and in the increased toughness. The epoxide-containing copolymers with 55 or 86% of BA units were also insufficient modifiers. The addition of the former yielded cured resins with homogeneous structure, whereas that of the latter resulted in macroscopic phase separation between the rubber and the epoxy resin. |