Effects of Sr doping on the structure,magnetic properties and microwave absorption properties of LaFeO3 nanoparticles |
| |
| Affiliation: | 1. Solid State Research Laboratory, Department of Physics, Burdwan University, Burdwan, 713104, India;2. Institut des Molécules et Matériaux du Mans, IMMM UMR CNRS 6283, Le Mans Université, 72085, Le Mans Cedex 9, France;1. Department of Physics, Malaviya National Institute of Technology, Jaipur 302017, India;2. Materials Research Centre, Malaviya National Institute of Technology, Jaipur 302017, India;1. Institute of Research and Development, Duy Tan University, Da Nang, 550000, Viet Nam;2. Department of Physics and Technology, Thai Nguyen University of Sciences, Thai Nguyen, Viet Nam;3. Institute of Materials Science, 18 Hoang-Quoc-Viet, Hanoi, Viet Nam;4. Faculty of Fundamental Sciences, Thai Nguyen University of Technology, Thai Nguyen, Viet Nam;5. Ceramics and Biomaterials Research Group, Advanced Institute of Materials Science, Ton Duc Thang University, Ho Chi Minh City, Viet Nam;6. Faculty of Applied Sciences, Ton Duc Thang University, Ho Chi Minh City, Viet Nam;1. Solid State Research Laboratory, Department of Physics, Burdwan University, Burdwan, 713104, India;2. Department of Spectroscopy, ICAS, Jadavpur, Kolkata, 700032, West Bengal, India;1. Department of Physical Sciences, Indian Institute of Science Education and Research, Berhampur 760100, Odisha, India;2. Department of Physics, Visvesvaraya National Institute of Technology, Nagpur 440010, Maharashtra, India;3. Department of Materials Science and Metallurgical Engineering, Maulana Azad National Institute of Technology, Bhopal 462003, M.P., India |
| |
| Abstract: | Lightweight, broadband microwave absorbing materials, with strong absorption capacities, are an urgent demand for practical applications. The microstructural and microwave absorption properties of LaFeO3 samples prepared by a sol-gel method using different amounts of Sr are investigated systematically. X-ray diffraction and Rietveld refinement studies showed that Sr2+ doping can distort the crystal structure of LaFeO3, leading to lattice expansion and spin tilt of the Fe-O-Fe bond angle. The improvement of magnetic properties mainly originates from the synergistic effect of the bond angle spin tilt and crystal structure defects. Oxygen vacancies will be generated due to the fluctuations in the valence state of Fe3+ resulting from the substitution of La3+ by Sr2+ as deduced from the X-ray photoelectron spectroscopy analysis. The generation of oxygen vacancies, electronic hopping and polarization loss may be one of the main reasons for changes in the electromagnetic parameters. The minimum reflection loss (RL) of La1–xSrxFeO3 nanoparticles with the Sr doping of 0.2 can reach approximately -39.3 dB at 10 GHz for the thickness of 2.2 mm, and the effective absorption bandwidth (RL ≤ -10 dB) can reach approximately 2.56 GHz. In addition, the La1–xSrxFeO3 nanoparticles also can obtain better microwave absorbing performance in the C-band (4–8 GHz) with the minimum RL of -36.8 dB for the matching thickness of 3.0 mm and Sr content of 0.3. Consequently, La1–xSrxFeO3 nanoparticles are promising materials for use in a high-performance and adjustable electromagnetic wave absorber, particularly in C-band and X-band. |
| |
| Keywords: | Magnetic properties Electromagnetic wave absorption Reflection loss |
| 本文献已被 ScienceDirect 等数据库收录！ |
|