Effects of non-stoichiometric defects on the dielectric properties of (Ba0.5Sr0.5)xTiO3-ZnGa2O4 composite ceramics |
| |
| Affiliation: | 1. School of Physics and Optoelectronic Engineering, Nanjing University of Information Science & Technology, 210044 Nanjing, China;2. State Key Laboratory of New Ceramics and Fine Processing, School of Materials Science and Engineering, Tsinghua University, 100084 Beijing, China;3. School of Materials Science and Engineering, Shijiazhuang Tiedao University, 050043 Shijiazhuang, China;4. The Department of Stomatology, The Second Hospital of Jilin University, 130041 Changchun, China;1. Key laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, 1295 Dingxi Road, Shanghai 200050, People''s Republic of China;2. Kunming Institute of Physics, Kunming 650223, People''s Republic of China |
| |
| Abstract: | In order to explore the effects of non-stoichiometric defects on the dielectric properties of composite ceramics, 70 wt% (Ba0.5Sr0.5)xTiO3-30 wt%ZnGa2O4 ((BS)xT50-ZG, x = (Ba + Sr)/Ti = 0.99, 1.00, 1.01 and 1.05) composite ceramics were fabricated by the traditional sintering technique. The association between structure and dielectric properties has been studied. The results show that the distortion of the crystal lattice brought by the partial Schottky defects, namely V″Ba,Sr–V˙˙O]× and V′′′′Ti–2V˙˙O]×, induces a decrease in the Curie temperature of (BS)xT50-ZG composite ceramics. The orientation of the elastic dipoles brought by oxygen vacancies causes the pinning of the domain walls, which reduces the dielectric loss at low frequencies. Tunability is related to the dipole polarization caused by V″Ba,Sr–V˙˙O]× and V′′′′Ti–2V˙˙O]× defect complexes. In addition, compared with the composite ceramic with x = 1, the Q values of the composite ceramics with x < 1 and x > 1 decreases due to the deterioration of the microstructure homogeneity and the enhancement of the disorder of the B-site cations in (BS)xT50. |
| |
| Keywords: | Non-stoichiometric defects Composite ceramics Dielectric properties |
| 本文献已被 ScienceDirect 等数据库收录！ |
|