Comparison of two cohost systems for doped red organic light-emitting devices in an effort to improve the efficiency and the lifetime

Blue-emitting 2-methyl-9,10-di(2-napthyl)anthracene (MADN) and yellow-emitting 5,6,11,12-tetraphenylnaphthacene (rubrene) were used as cohost materials together with tris(8-hydroxyquinolinato)aluminum (Alq₃) to form emission layers doped with the red dopant molecule 4-(dicyanomethylene)-2-t-butyl-6-(1,1,7,7-tetramethyljulolidyl-9-enyl)-4H-pyran (DCJTB). DCJTB-doped red organic light-emitting diodes based on both cohost systems showed remarkable improvements in terms of efficiency compared to DCJTB-doped Alq₃ single-host devices. With 2% DCJTB doping, the respective efficiencies of Alq₃ single-host, Alq₃ (60%)/rubrene (40%)-, and Alq₃ (20%)/MADN (80%)-cohost devices were 1.79, 4.44 and 5.42 cd/A at 20 mA/cm². Unlike Alq₃/rubrene-cohost devices, which experienced substantial current-induced quenching, Alq₃/MADN-cohost devices showed only a slight efficiency change at high current densities. At the luminance of 7680 cd/m², which was the benchmark for a practical passive-matrix OLED array with 64 scan-lines, an aperture ratio of 50%, and a polarizer transmittance of 50%, the power efficiency of the 2% DCJTB Alq₃/MADN-cohost device was 4.1 and 1.5 times better than that of Alq₃ single-host and Alq₃/rubrene-cohost devices, respectively. Moreover, the half-decay lifetime of the Alq₃/MADN-cohost device, measured as 14,000 h at an initial luminance of 1000 cd/m², was 4.4 and 1.9 times longer than the respective half-decay lifetimes of Alq₃ single-host and Alq₃/rubrene-cohost devices.