Bearing Fatigue Life Tests of Two Advanced Base Oils for Space Applications Under Vacuum and Atmospheric Environments

Four series of rolling-element bearing fatigue tests were conducted with 51104 size thrust ball bearings with three balls made from SUJ2 (AISI 52100) steel lubricated with two advanced synthetic base oils used for space applications. The test lubricants were perfluoropolyether (PFPE) and multiply alkyated cyclopentane (MAC). Each oil was tested with bearings under vacuum and atmospheric environments. The bearings were tested at a maximum Hertzian stress of 4 GPa on the inner and outer races. The outer race was rotated at a speed of 250 rpm. A pool lubrication system was used. Fresh lubricant was used for each test bearing. Testing in vacuum conditions was at 5 × 10^?2 Pa. The test oils were analyzed to determine whether changes occurred as a result of operating in air and in a vacuum. In a vacuum environment, the PFPE 815Z oil exhibited a longer fatigue life than the MAC 2001A oil. However, in an air environment, the MAC 2001A oil had a longer L₁₀ fatigue life than the PFPE 815Z oil. The fatigue life tests of PFPE 815Z oil in vacuum resulted in a longer L₁₀ life than when tested in an air environment. In an air environment, hydrogen fluoride was generated in the bearing tests with the PFPE 815Z oils. Under vacuum conditions, hydrogen fluoride was not generated with the PFPE 815Z oil, resulting in longer bearing fatigue lives. The fatigue life tests of MAC 2001A oil in a vacuum resulted in shorter L₁₀ fatigue life than in an air environment. The shorter life was attributed to the lower elastohydrodynamic oil film formation with the MAC 2001A oil because of a higher operating temperature and decomposition of the oil in vacuum.