Reciprocating Sliding Wear Performance of Hard Coating on Modified Titanium Alloy Surfaces
Authors:M Prem Ananth  R Ramesh
Affiliation:Department of Mechanical Engineering, Sri Venkateswara College of Engineering, Sriperumbudur, Chennai 602117, Tamilnadu, India
Abstract:The high strength, low weight, and outstanding corrosion resistance properties possessed by titanium alloys have led to a wide range of successful applications in aerospace, automotive, and chemical industries and in power generation. Titanium alloys are characterized by poor wear resistance properties and their utilization has been excessive in nontribological applications. Surface texturing is a well-known and effective means of surface modification to improve the tribological properties of sliding surfaces. In the present work, modification of titanium alloy surfaces (Ti6Al4V) was done by lapping and laser surface texturing. The wear-resistant coating, AlCrN, was applied over the modified titanium alloy surfaces, with and without a chromium interlayer. Linear reciprocating sliding wear tests were performed with ball-on-flat contact geometry to evaluate the tribological performance of the coated alloy. The tests were performed under different normal loads for a period of 105 cycles at a frequency of 5 Hz. The friction force between the contact pair and displacement of the ball were simultaneously observed using a force transducer and laser displacement sensor. Optical microscopy was used to quantify the wear volume by measuring the wear scar diameter on both the specimen and the counterbody. Scanning electron microscopy (SEM) was employed to study the morphology of the wear scar. The characteristic behavior of the AlCrN coating such as bonding strength, wear volume, wear rate, and coefficient of friction with the chromium interlayer was evaluated and compared with the coating directly applied over the substrate. The coating on the textured surface, with the chromium interlayer showed better tribological performance.
Keywords:Texturing  Chromium Interlayer  Bonding Strength  Reciprocating Wear  Coefficient of Friction  Wear Rate  Normal Load
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号