Synthesis, characterization and magnetoresistance properties study of magnetite thin films by electroless plating in aqueous solution

Polycrystalline half-metallic Fe₃O₄ films with 1 μm in thickness were synthesized on glass substrates directly by electroless plating in aqueous solution at 90 °C without heat treatment. The films have single pure spinal phase structure and the well-crystallized columnar grains grow perpendicularly to the substrates, as revealed by XRD, XPS and SEM. At room temperature, the films exhibit negative magnetoresistance (MR) ratio of about −5.1%, which is ascribed to intergranular tunneling of spin polarized electrons of Fe₃O₄. The resistivity R of the films with 1 μm in thickness at room temperature is about 5.2 × 10⁻¹ Ω cm. The cation distribution and the arrangement of the magnetic moments of the plated Fe₃O₄ ferrite thin films are different from that of the bulk materials, which is likely to be one of the reasons for the modification of R and MR properties.