Summary: Polystyrene (PS) was toughened with ethylene‐propylene‐diene terpolymer (EPDM) in the presence of styrene‐butadiene‐styrene block copolymer (SBS). Incorporation of SBS into the PS/EPDM blends clearly improved the impact properties. For PS/EPDM/SBS (mass ratio: 69/21/10) blends, the notched Charpy impact strength reached a maximum value of 26.3 kJ/m2. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) showed that SBS was distributed on the interface between PS and EPDM. Butanone extraction and FTIR analysis found that there was a grafting reaction between PS and EPDM phase during melt compounding. Shearing and processing rheological behaviors of blends were evaluated with a Haake capillary rheometer and a torque rheometer, respectively.