Preparation and evaluation of nanocomposites of polyfuran with Al2O3 and montmorillonite clay

High yield oxidative polymerization of furan was accomplished in CHCl₃ solvent at 0 °C. A nanocomposite of polyfuran (PF)–Al₂O₃ was prepared through polymerization of furan in a suspension of nanodimensional Al₂O₃ in CHCl₃ at 0 °C. High yield polymerization of furan was also achieved in montmorillonite clay (MMT) without any extraneous oxidant. The formation of PF was confirmed by FTIR and elemental analysis. Thermogravimetric analyses revealed the following trends in thermal stability: PF < PF–Al₂O₃ < Al₂O₃ and PF < PF–MMT < MMT. Scanning electron microscopy showed the average particles sizes to be ca 51 nm and ca 40 nm for PF–Al₂O₃ and PF–MMT composites, respectively. The occurrence of a peak at 19.84 Å in the X‐ray diffraction pattern of the PF–MMT composite was indicative of the intercalation of PF in MMT lamellae. Transmission electron microscopic analyses for the PF–MMT composite also showed incorporation of PF moieties in‐between the MMT layers. The dc conductivity values (S cm^?1) of PF–FeCl₃, PF–Al₂O₃–FeCl₃, PF–MMT and PF–MMT–FeCl₃ systems were in the order of 10^?6, 10^?7, 10^?8 and 10^?7, respectively, and the values were significantly enhanced compared to the dc conductivity value of PF homopolymers (10^?11). Copyright © 2004 Society of Chemical Industry