Ti5Nb人工钉扎中心NbTi超导体的磁通钉扎机制分析
引用本文:刘洪涛 吴晓祖 刘向宏 蒲明华 周廉 E.Mossang A.Sulpice. Ti5Nb人工钉扎中心NbTi超导体的磁通钉扎机制分析[J]. 稀有金属材料与工程, 2004, 33(3): 229-233
作者姓名:刘洪涛 吴晓祖 刘向宏 蒲明华 周廉 E.Mossang A.Sulpice
作者单位:1. 东北大学,辽宁,沈阳,110004;西北有色金属研究院,陕西,西安,710016
2. 西北有色金属研究院,陕西,西安,710016
3. Centre National de La Recherche Scientifique, 38042, Grenoble, France
基金项目:国家自然科学基金资助项目(19974033)
摘    要:采用棒基组合的装配方法,用热挤压和冷加工相结合的工艺制备了岛状Ti5Nb人工钉扎中心NbTi超导体,其中Ti5Nb体积含量为10%。通过对此超导体进行详细的磁通钉扎机制分析,认为样品的磁通钉扎力特征主要由正常相钉扎和Δκ扎相结合的机制决定。根据分析的结果,采用多源标度方法,很好地拟合了不同线径样品的磁通钉扎力密度随磁场变化的曲线。拟合的结果表明:样品在较低场下的性能主要由正常相钉扎机制决定,而在较高场下的性能主要由Δκ钉扎机制决定。并且随着线径的减小,正常相钉扎力密度和Δκ钉扎力密度均有不同程度的提高。

关 键 词:NbTi多芯复合体 人工钉扎中心 NbTi超导体 正常相磁通钉扎机制 Δκ磁通钉扎机制 钉扎力
文章编号:1002-185X(2004)03-0229-05
修稿时间:2003-06-09

Flux Pinning Mechanism in Superconducting NbTi Composites with Ti5Nb Artificial Pinning Center
Liu Hongtao,Wu Xiaozu,Liu Xianghong,Pu Minghu,Zhou Lian E. Mossang,A. Sulpice. Flux Pinning Mechanism in Superconducting NbTi Composites with Ti5Nb Artificial Pinning Center[J]. Rare Metal Materials and Engineering, 2004, 33(3): 229-233
Authors:Liu Hongtao  Wu Xiaozu  Liu Xianghong  Pu Minghu  Zhou Lian E. Mossang  A. Sulpice
Abstract:Flux pinning mechanism in superconducting NbTi composites with Ti5wt%Nb artificial pinning center is analyzed in detail. The results show that Fp(B) mainly depends on normal metal pinning mechanism and Dk pinning mechanism. The results suggeste that both normal metal pinning mechanism and Dk pinning mechanism are very important. The value of Fp(B) in lower magnetic field is mainly dominated by normal metal pinning mechanism and the value of Fp(B) in higher magnetic field is mainly dominated by Dk pinning mechanism. The function value of Fp(B) dependant on normal metal pinning mechanism and Dk pinning mechanism increase respectively with the decrease of the wire diameter.
Keywords:NbTi multifilamentary composite  artificial pinning center  normal metal pining mechanism  Dk pinning mechanism Biography: Liu Hongtao   Candidate for Ph.D.   Department of Electronic Informatio