Preparation,structural and photocatalytic activity of Sn/Fe co-doped TiO2 nanoparticles by sol-gel method

Pure and Sn/Fe co-doped (0.2 at.% Sn and 0.6 at.% Fe, 0.6 at.% Sn and 0.2 at.% Fe, 1.0 at.% Sn and 1.0 at.% Fe) TiO₂ nanoparticles were synthesized via a sol-gel method and subsequently calcined at different temperatures. Furthermore, the particles were analyzed by TG-DSC, XRD, TEM, HRTEM, EDS, SAED and UV–Vis for investigating the influences of dopant and calcination temperature on the thermal effect, composition, morphology, energy band gap (E_g) and the degradation efficiency of methyl orange (MO) under various light irradiations respectively. Results indicated that Sn/Fe co-doping inhibited the crystallization transformation from anatase to rutile phase of TiO₂ and decreased the E_g. The increased calcination temperature and Sn/Fe co-doped effect brought about the abnormal grain growth of TiO₂ nanoparticles. 0.6 at.% Sn/0.2 at.% Fe and 1.0 at.% Sn/1.0 at.% Fe co-doped TiO₂ nanoparticles presented better photocatalytic performance than pure and 0.2 at.% Sn/0.6 at.% Fe co-doped TiO₂ nanoparticles under visible light irradiation mainly due to the decreased E_g. On the contrary, 0.2 at.% Sn and 0.6 at.% Fe co-doped TiO₂ nanoparticles calcined at 650 °C showed the most excellent photocatalytic performance under UV light irradiation, which was about twice as large as that of pure TiO₂ possibly due to the formed hybrid structure of anatase and rutile phase as well as the h⁺-mediated decomposition pathway.