Effect of nano- and micro-sized Si3N4 powder on phase formation,microstructure and properties of β′-SiAlON prepared by spark plasma sintering

The phase formation behavior of β′-SiAlON with the general formula Si_6-zAl_zO_zN_8-z was studied comprehensively for z values from 1 to 3 using spark plasma sintering (SPS) as the consolidation technique at synthesis temperatures from 1400 to 1700 °C. The samples were prepared close to the β′-SiAlON composition line: Si₃N₄ ? 4/3(AlN·Al₂O₃) in the phase diagram using (A) nano-sized amorphous Si₃N₄ and (B) micro-sized β-Si₃N₄ precursors. Field-emission scanning electron microscopy (FESEM) was used for microstructural analysis.Most compositions reached almost full density at all SPS temperatures. Compared with the micro-sized β-Si₃N₄ precursor, the nano-sized amorphous Si₃N₄ precursor accelerated the reaction kinetics, promoting the formation of dense β′-SiAlON + O′-SiAlON composites after SPS at synthesis temperatures of 1400–1500 °C. This resulted in very high values of Vickers hardness (Hv₁₀) = 18.2–19.2 GPa for the z = 1 composition related to the hardness of the O′-SiAlON component phase.In general, for samples synthesized from nano-sized amorphous Si₃N₄, which were almost fully dense, containing >95% β′-SiAlON, the hardness values were 13.4–13.8 GPa with a fracture toughness of 3.5–4.6 MPa m^1/2. For equivalent samples synthesized from micro-sized β-Si₃N₄, hardness was in the range 13.9–14.4 GPa with a fracture toughness of 4.3–4.5 MPa.m^1/2. These values are comparable with fully dense β′-SiAlONs, usually containing intergranular glass phase which has been sintered by HIP and other processes at much higher temperatures for longer times.