Processing and thermal properties of SrTiO3 /Ti3AlC2 ceramic nanocomposites

Modulating the thermal conductivity has been a pragmatic approach for the development of high-performance thermoelectric material and thereby a step forward towards commercialization. Despite some efforts, the reduction in thermal conductivity of SrTiO₃ ceramic has not been fully realized. In this work, Ti₃AlC₂ in 3, and 7 vol% were uniformly incorporated in SrTiO₃ through nanostructured powder processing. The pristine SrTiO₃ and composites powders were consolidated by the spark plasma sintering at 1200 °C under uniaxial pressure of 50 MPa. Thermal properties of the bulk samples were evaluated from room temperature to 750 K through laser flash analysis. The thermal conductivity of SrTiO₃ based composites decreases substantially with the addition of nanostructured Ti₃AlC₂ from the pristine SrTiO₃ bulk sample. The reduction in thermal conductivity of 7 vol% composites is more than 30% at room temperature and even higher at elevated temperatures from the SrTiO₃. The interface thermal resistance was estimated which indicates a dominant role in diminishing the thermal conductivities of the composites. The results suggest that the addition of Ti₃AlC₂ as a second phase and nanostructuring through ball milling has significantly altered the phonon scattering mechanisms through multiple factors and thereby contributed to reducing effective thermal conductivities of the composites. This, work provide a scalable and economical route for the development of high-performance thermoelectric material.