Thermochemical degradation of HfSiO4 by molten CMAS

The thermochemical degradation of hafnium silicate (HfSiO₄) was investigated with a molten calcium-magnesium-aluminosilicate (CMAS) glass relevant to gas turbine engine applications. Sintered HfSiO₄ coupons were fabricated, within which wells were drilled and filled with CMAS glass powder at a loading of ～35 mg/cm². Samples were heat treated at 1200°C, 1300°C, 1400°C, and 1500°C for 1 h, 10 h, and 50 h. At 1200°C and 1300°C, slow formation of a Ca₂HfSi₄O₁₂ cyclosilicate phase was observed at the HfSiO₄-CMAS interface. At 1300°C and higher, rapid infiltration of CMAS into the material along the grain boundaries was observed. Initial conjecture into CMAS degradation mechanisms of HfSiO₄ are presented herein.