Li+ and Sm3+ co-doped AgNbO3-based antiferroelectric ceramics for high-power energy storage

Ag_1-x-3yLi_xSm_yNbO₃ (x≤0.05, y≤0.05) (ALSN) antiferroelectric ceramics were successfully prepared via conventional solid-state reaction and sinter routes in oxygen atmosphere for improving the energy storage characteristic of pure AgNbO₃. The results indicate that all of the studied compositions display a pure orthorhombic antiferroelectric (AFE) perovskite structure, while their key parameters of electric-field-induced antiferroelectric-ferroelectric transition can be affected by Li⁺ or/and Sm³⁺ doping contents. The Sm³⁺ doping can enhance the stability of antiferroelectric state, giving rise to higher antiferroelectric-ferroelectric transition electric-field (E_F and E_B), while Li⁺ doping can reduce E_F and E_B for Sm³⁺ doped AgNbO₃ with low Sm³⁺ content (y≤0.03). When co-doping the same amounts of Li⁺ and Sm³⁺ at x=y≤0.03, both E_F and E_B almost remain unchanged. At x=y=0.05, the diffuse phase transition (DPT) behavior of antiferroelectric-paraelectric (AFE-PE) phase transition occurred, resulting in a “slim-like” double-polarization hysteresis with significantly enhanced E_F. Due to these features, both W_rec and η are improved compared with pure AgNbO₃. The W_rec and η with composition at x=y=0.05 is 2.33 J/cm³ and 58% under applying electric field of 240 kV/cm, respectively. The results suggest that building DPT behavior of AFE-PE phase transition could be an alternative strategy to improve the energy storage characteristic of AgNbO₃.