Microwave dielectric properties of Ca1-xBaxMgSi2O6 ceramics

Ca_1-xBa_xMgSi₂O₆(x = 0–0.4) ceramics were prepared through a traditional solid-state reaction sintering route with various sintering temperatures. The effects of substituting Ba²⁺ for Ca²⁺, the relative density, phase composition, crystal morphology, and microwave dielectric properties of Ca_1-xBa_xMgSi₂O₆ (x = 0–0.4) ceramics were thoroughly studied. X-ray diffraction patterns indicate a single phase was formed in the samples when x ≤ 0.2, and the second phase BaMg₂Si₂O₇ appeared at x = 0.4. As the amount of Ba²⁺ substitution increases, the Q×f value first increases and then decreases due to the combined effects of FWHM of peak v₁₁ and atomic packing density, and the ${\epsilon }_r$ value was increased continuously which was closely corrected with the relative density and molecular polarization. The ${\tau }_f$ value improved slightly with the substituting Ba²⁺ for Ca²⁺. Typically, the Ca_0.88Ba_0.12MgSi₂O₆ ceramic can be well sintered at 1275 °C for 4 h with a maximum relative density of 99.3%, and possesses optimal microwave dielectric properties: ${\epsilon }_r=7.49$, $Q\times f=64310$ GHz, ${\tau }_f=-44.02$ ppm/°C.