Influence of pyrolysis and melt infiltration temperatures on the mechanical properties of SiCf/SiC composites

In order to improve the degree of matrix densification of SiC_f/SiC composites based on liquid silicon infiltration (LSI) process, the microstructure and mechanical properties of composites according to various pyrolysis temperatures and melt infiltration temperatures were investigated.Comparing the microstructures of SiC_f/C carbon preform by a one-step pyrolysis process at 600 °C and two-step pyrolysis process at 600 and 1600 °C, the width of the crack and microcrack formation between the fibers and matrix in the fiber bundle increased during the two-step pyrolysis process. For each pyrolysis process, the density, porosity, and flexural strength of the SiC_f/SiC composites manufactured by the LSI process at 1450–1550 °C were measured to evaluate the degree of matrix densification and mechanical properties. As a result, the SiC_f/SiC composite that was fabricated by the two-step pyrolysis process and LSI process showed an 18% increase in density, 16%p decrease in porosity, and 150% increase in flexural strength on average compared to the composite fabricated by the one-step pyrolysis process.In addition, among the SiC_f/SiC specimens fabricated by the LSI process after the same two-step pyrolysis process, the specimen that underwent the LSI process at 1500 °C showed 30% higher flexural strength on average than those at 1450 or 1550 °C. Furthermore, under the same pyrolysis temperature, the mechanical strength of SiC_f/SiC specimens in which the LSI process was performed at 1500 °C was higher than that of the 1550 °C although both porosity and density were almost similar. This is because the mechanical properties of the Tyranno-S grade SiC fibers degraded rapidly with increasing LSI process temperature.