Role of MgO in lowering glass transition temperature and increasing hardness of lithium silicate glass and glass-ceramics

The effect of variation of MgO (1.5, 4.5 and 7.5 mol%) content on glass structure, crystallization behavior, microstructure and mechanical properties in a Li₂O–K₂O–Na₂O–CaO–MgO–ZrO₂–Al₂O₃–P₂O₅–SiO₂ glass system has been reported here. Increased amount of MgO enhanced the participation of Al₂O₃ as a glass network former along with SiO₄] tetrahedra, reducing the amount of non-bridging oxygen (NBO) and increasing bridging oxygen (BO) amount in glass. The increased BO in glass resulted in a polymerized glass structure which suppressed the crystallization and subsequently increased the crystallization temperature, bulk density, nano hardness, elastic modulus in the glasses as well as the corresponding glass-ceramics. MgO addition caused phase separation in higher MgO (7.5 mol%) containing glass system which resulted in larger crystals. The nano hardness (～10 GPa) and elastic modulus (～127 GPa) values were found to be on a much higher side in 7.5 mol% MgO containing glass-ceramics as compared to lower MgO containing glass-ceramics.