Synthesis and photoluminescence performance of single-component Ca3YAl3B4O15:Dy3+, Eu3+ white-emitting phosphor for white light-emitting diodes

A single-component Ca₃YAl₃B₄O₁₅ (CYAB):Dy³⁺, Eu³⁺ phosphor was synthesized by the traditional high temperature solid-phase method, Dy³⁺ and Eu³⁺ were codoped in the structure to obtain a warm white emission. The results of XRD and EDS revealed that all samples had the standard Ca₃YAl₃B₄O₁₅ structure, and no impurity phase appeared with codoping. The emission of Dy³⁺ in CYAB consisted of both main peaks at 476 nm and 570 nm, with which a white emission could be observed. Furthermore, a characteristic emission peak of Eu³⁺ appeared at 617 nm in Dy³⁺/Eu³⁺-codoped samples to supplement red component for the white emission of Dy³⁺, due to the energy transfer effect between Dy³⁺ and Eu³⁺. With the amount of Eu³⁺ raised, the correlated colour temperature of CYAB:Dy³⁺, Eu³⁺ phosphor obviously decreased, and a warm white light was successfully realized from the manufactured w-LEDs. Therefore, all results indicated that the single-component Dy³⁺/Eu³⁺ codoped CYAB white-emitting phosphor had a potential application in ultraviolet excited w-LEDs.