Synthesis of a low-firing BaSi2O5 microwave dielectric ceramics with low dielectric constant

In this study, BaSi₂O₅ ceramics with an orthorhombic structure were synthesized by using a traditional solid-state method at a low temperature by doping with Li₂O–B₂O₃–CaO–CuO (LBCC) glass. The phase composition, mechanism of low-temperature sintering, microwave dielectric properties, and changes in the mesophase during the heating of low-temperature sintered BaSi₂O₅ ceramics were examined by performing an X-ray diffraction analysis. A compact matrix of BaSi₂O₅ can be wetted by the liquid phase of the formed LBCC glass. Therefore, LBCC glass with different doping percentages can effectively reduce the sintering temperature of BaSi₂O₅. The microwave dielectric properties of BaSi₂O₅ ceramics sintered at 900 °C at 4 wt% of LBCC glass were determined: ε_r = 7.32, Q × f = 19,002 GHz, and τ_f = ?35.8 ppm/°C. The chemical compatibility of the samples with Ag was studied at 4 wt% doping with LBCC glass, and the samples were fired for 4 h at 900 °C.