Effect of silica sol on performance and surface precision of alumina ceramic shell prepared by binder jetting

Using 3D printing technology to prepare ceramic shell used for precision investment casting can realize short process and efficient preparation of the ceramic shell, which has a great application potential in the casting field. However, the 3D printed ceramic shells often have the problems of low strength and accuracy. In this paper, a silica sol room temperature dip coating treatment combined with high temperature sintering method was proposed to improve the strength and surface precision of the ceramic shell prepared by the binder jetting. The effects of silica sol concentration and dip coating time on performance and surface precision of the alumina ceramic shell were studied. The mechanical properties and surface precision of the alumina ceramic shell prepared by the binder jetting were improved significantly with the increases of the sol concentration and dip coating time. With the dip coating time of 90 s and sol concentration of 30%, the maximum bending strength of the alumina ceramic reached 44.8 MPa, which was 18.9 times higher than that of the untreated alumina ceramic. The top surface roughness and side roughness of the alumina ceramic decreased from 6.87 μm to 5.70 μm and 7.55 μm–6.46 μm, respectively, compared to those of the untreated alumina ceramic.